BASF Ultramid® 1003-2 NF2002 PA66 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 1003-2 NF2002 PA66 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 1003-2 NF2002 is a general purpose, heat stabilized nylon 6/6.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
dry; ISO 1183
Water Absorption 8.5 %
8.5 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 2.5 %
2.5 %
beginning dry (23°C/50% R.H.); ISO 62
Linear Mold Shrinkage 0.016 cm/cm
0.016 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 54.0 MPa
7830 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 25 %
25 %
50mm/min; ISO 527
Tensile Modulus 1.25 GPa
181 ksi
1mm/min; ISO 527
Flexural Modulus 1.15 GPa
167 ksi
ISO Data
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO Test
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
ISO 179
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Thermal Properties Metric English Comments
Melting Point 257 °C
495 °F
10 K/min
257 °C
495 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding