Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

BASF Ultraform W 2320 003 BK120 Q600 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform W
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform W 2320 003 BK120 Q600 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultraform W 2320 003 BK120 Q600 is a pigmented black, very easy flowing and rapidly solidifying injection molding POM grade for use where processing is extremely difficult but mechanical properties are lower. Contains a mold release agent. It conforms to FDA requirements of 21 CFR 177.2470.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.019 cm/cm
0.019 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 63.0 MPa
9140 psi
50mm/min; ISO 527
Elongation at Yield 7.5 %
7.5 %
50mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1mm/min; ISO 527
Flexural Modulus 2.60 GPa
377 ksi
ISO Data
Izod Impact, Notched (ISO) 5.50 kJ/m²
2.62 ft-lb/in²
ISO Test
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Melting Point 167 °C
333 °F
10 K/min
167 °C
333 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
ISO 75
Descriptive Properties Value Comments
Color BK120
Commercial Status Active America
FDA 21 CFR 177.2470
Impact Modified No
Primary Processing Technique Injection Molding