BASF Ultraform® N2520 XL2 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer BASF
Trade Name Ultraform®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform® N2520 XL2 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Is a POM, injection-molding grade with increased electrical conductivity, for applications with reduced mechanical requirements.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.850 g/cc
0.0307 lb/in³
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C; 50% RH; ISO 62
Melt Flow 7.579 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.579 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 179 MPa

@Load 98.0 kg,
Time 30.0 sec
26000 psi

@Load 216 lb,
Time 0.00833 hour
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
5 mm/min; ISO 527-2
Elongation at Break 1.5 %
1.5 %
Nominal, 50 mm/min; ISO 527-2
Modulus of Elasticity 3.00 GPa
435 ksi
ISO 527-2
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
2.40 J/cm²

@Temperature 23.0 °C
11.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C

@Temperature 23.0 - 55.0 °C
66.7 µin/in-°F

@Temperature 73.4 - 131 °F
DIN 53752
Melting Point 166 °C
331 °F
DIN 53765
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
ISO 75-2
Vicat Softening Point 150 °C
302 °F
ISO 306
Decomposition Temperature >= 240 °C
>= 464 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 0.20 ohm-cm
0.20 ohm-cm
IEC 60093
Surface Resistance 3000 ohm
3000 ohm
IEC 60093
Processing Properties Metric English Comments
Processing Temperature 200 °C
392 °F
Hopper Throat
Zone 1 200 °C
392 °F
Feed zone
Zone 2 200 °C
392 °F
Compression
Zone 3 200 °C
392 °F
Metering-zone
Zone 4 200 °C
392 °F
Nozzle
Melt Temperature 200 °C
392 °F
Optimal
190 - 220 °C
374 - 428 °F
Injection-molding
Mold Temperature 90.0 °C
194 °F
Optimal
60.0 - 120 °C
140 - 248 °F
Injection-molding
Drying Temperature 100 °C
212 °F
Dry Time 3 hour
3 hour
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature 320 - 340°C
ASTM D1929
Peripheral screw speed <0.3 m/s
Primary Processing Technique Injection Molding