BASF Ultraform N 2640 Z4 BK140 Q600 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified
Manufacturer BASF
Trade Name Ultraform N
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultraform N 2640 Z4 BK140 Q600 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultraform N2640 Z4 BK140 Q600 is a high toughness, elastomer-modified injection molding POM grade.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
Water Absorption 0.80 %
0.80 %
ISO 62
Moisture Absorption at Equilibrium 0.25 %
0.25 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.019 cm/cm
0.019 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 MPa
5220 psi
50mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 14 %
14 %
50mm/min; ISO 527
Tensile Modulus 1.55 GPa
225 ksi
1mm/min; ISO 527
Flexural Modulus 1.57 GPa
228 ksi
ASTM Test
1.74 GPa
252 ksi
ISO Data
Izod Impact, Notched 0.950 J/cm

@Thickness 3.17 mm
1.78 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO) 11.7 kJ/m²
5.57 ft-lb/in²
ISO Test
Thermal Properties Metric English Comments
Melting Point 167 °C
333 °F
10 K/min
167 °C
333 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ASTM Test
Descriptive Properties Value Comments
Color BK140
Commercial Status Active America
Impact Modified Yes
Primary Processing Technique Injection Molding