- BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT
BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultradur S |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur S 4090 G6 LS High Speed BK15077 30% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultradur S 4090 G6 LS High Speed BK15077 is a high flow, fast cycling with low warpage, 30% glass filled injection molding PBT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Viscosity Test | 102 cm³/g | 102 cm³/g | Viscosity number |
| Melt Flow | 33.9 g/10 min @Load 2.16 kg, Temperature 275 °C |
33.9 g/10 min @Load 4.76 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5mm/min; ISO 527 |
| Tensile Modulus | 9.90 GPa | 1440 ksi | 1mm/min; ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10 K/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK15077 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |