BASF Ultradur B 4406 G4 Q113 20% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer BASF
Trade Name Ultradur B
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur B 4406 G4 Q113 20% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur B4406 G4 Q113 is an UL V0 injection molding PBT grade with 20% glass fiber reinforcement.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Viscosity Test 112 cm³/g
112 cm³/g
Viscosity number
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Melt Flow 11 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 11 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa
17000 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 117 MPa
17000 psi
5mm/min; ISO 527
Elongation at Break 2.2 %
2.2 %
5mm/min; ISO 527
2.2 %
2.2 %
Tensile Modulus 8.28 GPa
1200 ksi
ASTM Test
8.35 GPa
1210 ksi
1mm/min; ISO 527
Izod Impact, Notched 0.530 J/cm

@Thickness 3.17 mm
 0.993 ft-lb/in

@Thickness 0.125 in
 ASTM Test
Charpy Impact Unnotched 3.60 J/cm²
17.1 ft-lb/in²
ISO 179
5.00 J/cm²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear 30.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 16.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM Test
CTE, linear, Parallel to Flow 50.0 µm/m-°C
27.8 µin/in-°F
ISO 11359
Melting Point 223 °C
433 °F
10 K/min
223 °C
433 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ASTM Test
215 °C
419 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 177 °C
351 °F
ASTM Test
180 °C
356 °F
ISO 75
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
 3.5

@Frequency 1.00e+6 Hz
 IEC 60250
3.7

@Frequency 100 Hz
 3.7

@Frequency 100 Hz
 IEC 60250
Dissipation Factor 0.0016

@Frequency 100 Hz
 0.0016

@Frequency 100 Hz
 IEC 60250
0.017

@Frequency 1.00e+6 Hz
 0.017

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 200 V
200 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 265 °C
509 °F
Injection molding
Injection Velocity 70.0 mm/sec
2.76 in/sec
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Flame retarding agent
Heat stabilized or stable to heat
Light stabilized or stable to light
Lubricant
U.V. stabilized or stable to weather