BASF Ultradur B 4300 G6 30% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur B
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur B 4300 G6 30% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur B4300 G6 is an easy flowing injection molding PBT with 30% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.Applications: Program switches, thermostat parts, small-motor housings for vehicles, headlamp frames, cams, automotive windscreen wiper arms, PCBs, housings, consoles, contact mounts and covers.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
DIN 53495/1L
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.
Viscosity Test 102 cm³/g
102 cm³/g
Viscosity number; ISO 1628
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Sheet
0.0034 cm/cm
0.0034 in/in
60x60x2mm; ISO 294
Linear Mold Shrinkage, Transverse 0.0107 cm/cm
0.0107 in/in
60x60x2mm; ISO 294
0.011 cm/cm
0.011 in/in
Sheet
Melt Flow 16.8 g/10 min

@Load 2.16 kg,
Temperature 250 °C
16.8 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 190 MPa
27600 psi
ISO 2039-1
Tensile Strength at Break 135 MPa
19600 psi
5mm/min; ISO 527-2
Tensile Strength 75.0 MPa

@Temperature 100 °C
10900 psi

@Temperature 212 °F
ISO 527
100 MPa

@Temperature 50.0 °C
14500 psi

@Temperature 122 °F
ISO 527
140 MPa

@Temperature 23.0 °C
20300 psi

@Temperature 73.4 °F
ISO 527
170 MPa

@Temperature -20.0 °C
24700 psi

@Temperature -4.00 °F
ISO 527
Tensile Stress 40.0 MPa

@Strain 0.500 %,
Temperature 40.0 °C
5800 psi

@Strain 0.500 %,
Temperature 104 °F
ISO 527
40.0 MPa

@Strain 2.00 %,
Temperature 140 °C
5800 psi

@Strain 2.00 %,
Temperature 284 °F
ISO 527
50.0 MPa

@Strain 4.00 %,
Temperature 140 °C
7250 psi

@Strain 4.00 %,
Temperature 284 °F
ISO 527
50.0 MPa

@Strain 0.500 %,
Temperature -40.0 °C
7250 psi

@Strain 0.500 %,
Temperature -40.0 °F
ISO 527
52.0 MPa

@Strain 5.00 %,
Temperature 140 °C
7540 psi

@Strain 5.00 %,
Temperature 284 °F
ISO 527
100 MPa

@Strain 2.00 %,
Temperature 40.0 °C
14500 psi

@Strain 2.00 %,
Temperature 104 °F
ISO 527
105 MPa

@Strain 3.00 %,
Temperature 40.0 °C
15200 psi

@Strain 3.00 %,
Temperature 104 °F
ISO 527
170 MPa

@Strain 2.00 %,
Temperature -40.0 °C
24700 psi

@Strain 2.00 %,
Temperature -40.0 °F
ISO 527
200 MPa

@Strain 3.00 %,
Temperature -40.0 °C
29000 psi

@Strain 3.00 %,
Temperature -40.0 °F
ISO 527
20.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
2900 psi

@Strain 1.00 %,
Time 1000 hour
140°C; DIN 50014-23/50-2
25.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
3630 psi

@Strain 1.00 %,
Time 1000 hour
100°C; DIN 50014-23/50-2
30.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
4350 psi

@Strain 1.00 %,
Time 1000 hour
60°C; DIN 50014-23/50-2
30.0 MPa

@Strain 2.00 %,
Time 3.60e+6 sec
4350 psi

@Strain 2.00 %,
Time 1000 hour
140°C; DIN 50014-23/50-2
35.0 MPa

@Strain 3.00 %,
Time 3.60e+6 sec
5080 psi

@Strain 3.00 %,
Time 1000 hour
140°C; DIN 50014-23/50-2
35.0 MPa

@Strain 2.00 %,
Time 3.60e+6 sec
5080 psi

@Strain 2.00 %,
Time 1000 hour
100°C; DIN 50014-23/50-2
40.0 MPa

@Strain 3.00 %,
Time 3.60e+6 sec
5800 psi

@Strain 3.00 %,
Time 1000 hour
100°C; DIN 50014-23/50-2
40.0 MPa

@Strain 0.600 %,
Time 3.60e+6 sec
5800 psi

@Strain 0.600 %,
Time 1000 hour
DIN 50014-23/50-2
55.0 MPa

@Strain 2.00 %,
Time 3.60e+6 sec
7980 psi

@Strain 2.00 %,
Time 1000 hour
60°C; DIN 50014-23/50-2
60.0 MPa

@Strain 1.00 %,
Time 3.60e+6 sec
8700 psi

@Strain 1.00 %,
Time 1000 hour
DIN 50014-23/50-2
80.0 MPa

@Strain 1.60 %,
Time 3.60e+6 sec
11600 psi

@Strain 1.60 %,
Time 1000 hour
DIN 50014-23/50-2
Elongation at Break 2.5 %
2.5 %
5mm/min; ISO 527-2
Modulus of Elasticity 10.0 GPa
1450 ksi
ISO 527-2
Flexural Strength 200 MPa
29000 psi
ISO 178
Charpy Impact Unnotched 6.70 J/cm²
31.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.24 ft-lb/in²
ISO 179/1eA
Dart Drop, Total Energy <= 5.00 J
<= 3.69 ft-lb
ISO 6603-1
Tensile Creep Modulus, 1000 hours 7500 MPa
1.09e+6 psi
ISO 899
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 2.00 - 3.00 µm/m-°C

@Temperature 23.0 - 80.0 °C
1.11 - 1.67 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 53752
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
IEC 1006
Thermal Conductivity 0.270 W/m-K
1.87 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 - 225 °C
428 - 437 °F
ISO 11357-3
Maximum Service Temperature, Air 140 °C
284 °F
at 50% loss of tensile strength after 20000h; IEC 216-1
160 °C
320 °F
at 50% loss of tensile strength after 5000h; IEC 216-1
210 °C
410 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
ISO 75
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Flame Spread <= 100 mm/min
<= 3.94 in/min
DIN 75200
Glow Wire Test <= 750 °C

@Thickness 3.00 mm
<= 1380 °F

@Thickness 0.118 in
IEC 695
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
IEC 60250
4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 100 kV/mm
2540 kV/in
IEC 243/1
Dissipation Factor 0.0025

@Frequency 100 Hz
0.0025

@Frequency 100 Hz
IEC 60250
0.017

@Frequency 1.00e+6 Hz
0.017

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
Test Solution B; IEC 112
375 V
375 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
250 - 275 °C
482 - 527 °F
Injection molding
Mold Temperature 60.0 - 100 °C
140 - 212 °F