BASF Ultradur B 4300 G3 15% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur B
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur B 4300 G3 15% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur B 4300 G3 is an easy flowing injection molding PBT with 15% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Viscosity Test 111 cm³/g
111 cm³/g
Viscosity number
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM Data; MD
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 22 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 93.0 MPa
13500 psi
0.2 in/min; ASTM Test
Tensile Strength, Ultimate 93.0 MPa
13500 psi
5mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
5mm/min; ISO 527
4.0 %
4.0 %
0.2 in/min; ASTM Test
Tensile Modulus 5.52 GPa
801 ksi
ASTM Test
6.00 GPa
870 ksi
1mm/min; ISO 527
Flexural Modulus 4.80 GPa
696 ksi
ISO Data
4.83 GPa
701 ksi
ASTM Test
Izod Impact, Notched 0.430 J/cm

@Temperature -40.0 °C
 0.806 ft-lb/in

@Temperature -40.0 °F
 ASTM Test
0.530 J/cm

@Thickness 3.17 mm
 0.993 ft-lb/in

@Thickness 0.125 in
 ASTM Test
Izod Impact, Notched (ISO) 8.50 kJ/m²
4.04 ft-lb/in²
ISO Test
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359
Melting Point 223 °C
433 °F
10 K/min
223 °C
433 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ASTM Test
220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 183 °C
361 °F
ISO 75
203 °C
397 °F
ASTM Test
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
 HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 3.7

@Frequency 100 Hz
 3.7

@Frequency 100 Hz
 IEC 60250
3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.0012

@Frequency 100 Hz
 0.0012

@Frequency 100 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
Processing Properties Metric English Comments
Melt Temperature 265 °C
509 °F
Injection molding
Injection Velocity 70.0 mm/sec
2.76 in/sec
Injection molding
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
NSF Std. 61 Yes
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
Light stabilized or stable to light
Lubricant
U.V. stabilized or stable to weather