BASF Ultradur® B 4040 G10 50% Glass Filled BK 15029 PBT + PET

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET)
Manufacturer BASF
Trade Name Ultradur®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur® B 4040 G10 50% Glass Filled BK 15029 PBT + PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection molding grade with 50% glass fibers for industrial parts with excellent surface quality, for example external door handles in vehicles, visible sunroof frames, oven door handles, toaster casings, external mirrors, rear screen wiper arms in vehicles and sunroof wind deflectors.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.600 - 0.900 g/cc
0.0217 - 0.0325 lb/in³
Density 1.73 g/cc
0.0625 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
ISO 62
Viscosity Measurement 90
90
[cm<sup>3</sup>/g]; ISO 307
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
plate with film gate 150x150x3mm<sup>3</sup>
0.0024 cm/cm
0.0024 in/in
ISO 2577
Linear Mold Shrinkage, Transverse 0.0075 cm/cm
0.0075 in/in
plate with film gate 150x150x3mm<sup>3</sup>
0.0077 cm/cm
0.0077 in/in
ISO 2577
Melt Flow 67.47 g/10 min

@Load 10.0 kg,
Temperature 275 °C
67.47 g/10 min

@Load 22.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 165 MPa
23900 psi
50 mm/min; ISO 527-1/-2
Elongation at Break 1.5 %
1.5 %
ISO 527-1/-2
Tensile Modulus 18.7 GPa
2710 ksi
ISO 527-1/-2
Charpy Impact Unnotched 5.20 J/cm²

@Temperature 23.0 °C
24.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
5.80 J/cm²

@Temperature -30.0 °C
27.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 - 30.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
11.1 - 16.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-1/-2
Melting Point 235 °C
455 °F
ISO 11357-1/-2
Maximum Service Temperature, Air 140 °C
284 °F
at 50% loss of tensile strength after 20,000hr
160 °C
320 °F
at 50% loss of tensile strength after 5,000hr
210 °C
410 °F
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-1/-2
Decomposition Temperature >= 290 °C
>= 554 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness >=0.400 mm
HB

@Thickness >=0.0157 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Dielectric Constant 4.5

@Frequency 1.00e+6 Hz
4.5

@Frequency 1.00e+6 Hz
IEC 60250
4.7

@Frequency 100 Hz
4.7

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0020

@Frequency 100 Hz
0.0020

@Frequency 100 Hz
IEC 60250
0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed zone
Zone 2 265 °C
509 °F
Compression
Zone 3 270 °C
518 °F
Metering-zone
Zone 4 270 °C
518 °F
Nozzle
Melt Temperature 250 - 280 °C
482 - 536 °F
Injection molding/Extrusion
270 °C
518 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
60.0 - 100 °C
140 - 212 °F
Injection molding
Drying Temperature 80.0 - 120 °C
176 - 248 °F
Dry Time 4 hour
4 hour
Moisture Content <= 0.040 %
<= 0.040 %
Descriptive Properties Value Comments
Color BK 15029
Commercial Status Europe
Ignition Temperature 350°C
ASTM D1929
Peripheral screw speed < 0.25 m/s