BASF Petra® 330 FR BK-112 30% Glass Filled PET

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant
Manufacturer	BASF
Trade Name	Petra®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Petra® 330 FR BK-112 30% Glass Filled PET.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding of thin and complex parts such as electrical bobbins. Due to its high crystallization rate the processability of the product in the injection molding process is very good. It exhibits excellent balance of properties including strength, stiffness, HDT, dimensional resistance and electrical properties.

Physical Properties	Metric	English	Comments
Density	1.67 g/cc	0.0603 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM Test
Tensile Strength at Break	135 MPa	19600 psi	0.2 in/min; ASTM Test
	60.0 MPa @Temperature 120 °C	8700 psi @Temperature 248 °F	ISO Data
	60.0 MPa @Temperature 120 °C	8700 psi @Temperature 248 °F	ASTM Test
	82.0 MPa @Temperature 80.0 °C	11900 psi @Temperature 176 °F	ASTM Test
	82.0 MPa @Temperature 80.0 °C	11900 psi @Temperature 176 °F	ISO Data
	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	ASTM Test
	170 MPa @Temperature -40.0 °C	24700 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	135 MPa	19600 psi	5mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	5mm/min; ISO 527
	2.0 %	2.0 %	0.2 in/min; ASTM Test
	2.0 % @Temperature -40.0 °C	2.0 % @Temperature -40.0 °F	ASTM Test
	2.0 % @Temperature -40.0 °C	2.0 % @Temperature -40.0 °F	ISO Data
	4.1 % @Temperature 80.0 °C	4.1 % @Temperature 176 °F	ASTM Test
	4.1 % @Temperature 80.0 °C	4.1 % @Temperature 176 °F	ISO Data
	5.7 % @Temperature 120 °C	5.7 % @Temperature 248 °F	ASTM Test
	5.7 % @Temperature 120 °C	5.7 % @Temperature 248 °F	ISO Data
Flexural Strength	215 MPa	31200 psi	ASTM Test
Flexural Modulus	9.93 GPa	1440 ksi	ASTM Test
Izod Impact, Notched	0.900 J/cm @Thickness 3.17 mm	1.69 ft-lb/in @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	250 °C	482 °F	10 K/min
	255 °C	491 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	223 °C	433 °F	ASTM Test
Flammability, UL94	V-0 @Thickness 0.300 mm	V-0 @Thickness 0.0118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.7 @Frequency 100 Hz	3.7 @Frequency 100 Hz	IEC 60250
	3.9 @Frequency 1.00e+6 Hz	3.9 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	34.0 kV/mm	864 kV/in	IEC 60243-1
Dissipation Factor	0.010 @Frequency 1.00e+6 Hz	0.010 @Frequency 1.00e+6 Hz	IEC 60250
	0.020 @Frequency 100 Hz	0.020 @Frequency 100 Hz	IEC 60250
Comparative Tracking Index	260 V	260 V	IEC 60112

Descriptive Properties	Value	Comments
Color	BK-112
Commercial Status	Active America
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes