BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass/Mineral Reinforced
Manufacturer	BASF
Trade Name	Petra®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Petra® 230 BK-112 22/13% Glass/Mineral Filled PET.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Petra 230 BK-112 is a 35% mineral and glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a very good combination of performance properties including high strength and stiffness with ductility at elevated temperatures, good chemical resistance, dimensional stability and warp resistance.

Physical Properties	Metric	English	Comments
Density	1.424 g/cc	0.05145 lb/in³	Melt; ISO 1183
	1.61 g/cc	0.0582 lb/in³	ISO 1183
Viscosity Measurement	0.55	0.55	Inherent Viscosity
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM Test
Tensile Strength at Break	115 MPa	16700 psi	0.2 in/min; ASTM Test
	45.0 MPa @Temperature 120 °C	6530 psi @Temperature 248 °F	ISO Data
	45.0 MPa @Temperature 120 °C	6530 psi @Temperature 248 °F	ASTM Test
	60.0 MPa @Temperature 80.0 °C	8700 psi @Temperature 176 °F	ASTM Test
	60.0 MPa @Temperature 80.0 °C	8700 psi @Temperature 176 °F	ISO Data
	145 MPa @Temperature -40.0 °C	21000 psi @Temperature -40.0 °F	ASTM Test
	145 MPa @Temperature -40.0 °C	21000 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	115 MPa	16700 psi	5mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	0.2 in/min; ASTM Test
	2.0 %	2.0 %	5mm/min; ISO 527
	1.6 % @Temperature -40.0 °C	1.6 % @Temperature -40.0 °F	ISO Data
	1.6 % @Temperature -40.0 °C	1.6 % @Temperature -40.0 °F	ASTM Test
	6.3 % @Temperature 80.0 °C	6.3 % @Temperature 176 °F	ASTM Test
	6.3 % @Temperature 80.0 °C	6.3 % @Temperature 176 °F	ISO Data
	8.1 % @Temperature 120 °C	8.1 % @Temperature 248 °F	ISO Data
	8.1 % @Temperature 120 °C	8.1 % @Temperature 248 °F	ASTM Test
Tensile Modulus	11.7 GPa	1700 ksi	1mm/min; ISO 527
	2.59 GPa @Temperature 120 °C	376 ksi @Temperature 248 °F	ISO Data
	4.12 GPa @Temperature 80.0 °C	598 ksi @Temperature 176 °F	ISO Data
	12.27 GPa @Temperature -40.0 °C	1780 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	180 MPa	26100 psi	ASTM Test
Flexural Modulus	8.76 GPa	1270 ksi	ISO Data
	9.05 GPa	1310 ksi	ASTM Test
Izod Impact, Notched	0.550 J/cm @Thickness 3.17 mm	1.03 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	ISO Test
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179
	0.550 J/cm² @Temperature -30.0 °C	2.62 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	22.0 µm/m-°C @Temperature -30.0 - 30.0 °C	12.2 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Specific Heat Capacity	1.906 J/g-°C	0.4555 BTU/lb-°F	Melt
Thermal Conductivity	0.306 W/m-K	2.12 BTU-in/hr-ft²-°F	Melt
Melting Point	245 °C	473 °F	10 K/min
	245 °C	473 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	240 °C	464 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	206 °C	403 °F	ASTM Test
	210 °C	410 °F	ISO 75

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	115 °C	239 °F	Injection molding
Injection Velocity	115 mm/sec	4.53 in/sec	Injection molding

Descriptive Properties	Value	Comments
Color	BK-112
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding