BASF Petra® 130 BK-112 30% Glass Filled PET

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer	BASF
Trade Name	Petra®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Petra® 130 BK-112 30% Glass Filled PET.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Petra 130 BK-112 is a 30% glass fiber reinforced, black pigmented polyethylene terephthalate injection molding compound. It exhibits a combination of performance properties including good strength and stiffness at elevated temperatures. It also has good chemical resistance and dimensional stability, and adequate ductility for most applications.

Physical Properties	Metric	English	Comments
Density	1.55 g/cc	0.0560 lb/in³	ISO 1183
Viscosity Measurement	0.55	0.55	Inherent Viscosity
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM Test
Tensile Strength at Break	145 MPa	21000 psi	0.2 in/min; ASTM Test
	54.0 MPa @Temperature 120 °C	7830 psi @Temperature 248 °F	ISO Data
	211 MPa @Temperature -40.0 °C	30600 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Ultimate	145 MPa	21000 psi	5mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5mm/min; ISO 527
	3.0 %	3.0 %	0.2 in/min; ASTM Test
	2.3 % @Temperature -40.0 °C	2.3 % @Temperature -40.0 °F	ISO Data
	4.0 % @Temperature 120 °C	4.0 % @Temperature 248 °F	ISO Data
Tensile Modulus	10.2 GPa	1480 ksi	1mm/min; ISO 527
Flexural Strength	230 MPa	33400 psi	ASTM Test
Flexural Modulus	8.25 GPa	1200 ksi	ISO Data
	8.76 GPa	1270 ksi	ASTM Test
Izod Impact, Notched	0.950 J/cm @Thickness 3.17 mm	1.78 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	9.50 kJ/m²	4.52 ft-lb/in²	ISO Test
	8.50 kJ/m² @Temperature -40.0 °C	4.04 ft-lb/in² @Temperature -40.0 °F	ISO Test
Charpy Impact, Notched	0.900 J/cm²	4.28 ft-lb/in²	ISO 179
	0.850 J/cm² @Temperature -30.0 °C	4.05 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	23.0 µm/m-°C @Temperature -30.0 - 30.0 °C	12.8 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
Melting Point	245 °C	473 °F	10 K/min
	245 °C	473 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	235 °C	455 °F	ASTM Test
	240 °C	464 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	ISO 75
	215 °C	419 °F	ASTM Test
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	115 °C	239 °F	Injection molding

Descriptive Properties	Value	Comments
Color	BK-112
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes