BASF Neopolen® P 9235 0.035 g/cc Core density; Expanded Polypropylene (Europe)

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Foamed
Manufacturer BASF
Trade Name Neopolen®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Neopolen® P 9235 0.035 g/cc Core density; Expanded Polypropylene (Europe).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Neopolen® P 9235 is expanded Polypropylene supplied in the form of beads. The cells are largely closed.Physical properties of moldings made from Neopolen® P 9235.Note: In order to measure the physical properties, parts with dimensions 300x200x60 mm were molded on a machine typical for the EPP industry under standard conditions. The properties can vary depending on part geometry and processing parameters.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.0300 - 0.0360 g/cc
0.00108 - 0.00130 lb/in³
Density 0.0350 g/cc
0.00126 lb/in³
ISO 845
Water Absorption <= 1.0 %

@Time 86400 sec
<= 1.0 %

@Time 24.0 hour
DIN 53428
Particle Size >= 1500 µm
>= 1500 µm
<= 4000 µm
<= 4000 µm
Mechanical Properties Metric English Comments
Tensile Strength 0.530 MPa
76.9 psi
DIN EN ISO 1798
Elongation at Break 34 %
34 %
DIN EN ISO 1798
Compressive Strength 0.150 MPa

@Strain 10.0 %
21.8 psi

@Strain 10.0 %
ISO 844
0.180 MPa

@Strain 25.0 %
26.1 psi

@Strain 25.0 %
ISO 844
0.280 MPa

@Strain 50.0 %
40.6 psi

@Strain 50.0 %
ISO 844
Compression Set 29 %

@Temperature 23.0 °C,
Time 79200 sec
29 %

@Temperature 73.4 °F,
Time 22.0 hour
50% RH; 24h after stress release; DIN EN ISO 1856 (Procedure C)
Thermal Properties Metric English Comments
Thermal Conductivity 0.0370 W/m-K
0.257 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 120 - 180 °C
248 - 356 °F
Decomposition Temperature >= 180 °C
>= 356 °F
Flash Point >= 200 °C
>= 392 °F
ASTM D1929
Descriptive Properties Value Comments
Average Particle Weight 0.6 - 1.0 mg
Color Black
Commercial Status Europe
Dimensional Stability at Heat <2%
Linear size alterations after 4 d, 110°C; DIN ISO 2796
Ignition Temperature > 360 °C
ASTM D1929