BASF Luranyl® KR 2456/3 Polyphenylene Ether + Styrene-Butadiene Blend

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend , Styrene-Butadiene
Manufacturer BASF
Trade Name Luranyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Luranyl® KR 2456/3 Polyphenylene Ether + Styrene-Butadiene Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Heat resistant grade containing halogen-free flame-retardant. Mainly used for functional electronic parts that must meet tough fire-safety legislation.Data was collected by ISO methods and provided by BASF.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
Water Absorption 0.40 %
0.40 %
Moisture Absorption at Equilibrium 0.15 %
0.15 %
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
High Load Melt Index 35 g/10 min

@Load 21.6 kg,
Temperature 250 °C
35 g/10 min

@Load 47.6 lb,
Temperature 482 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
Elongation at Break 20 %
20 %
Elongation at Yield 5.0 %
5.0 %
Tensile Modulus 2.80 GPa
406 ksi
Charpy Impact Unnotched NB
NB
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.60 J/cm²
7.61 ft-lb/in²
1.60 J/cm²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
Tensile Creep Modulus, 1000 hours 1950 MPa
283000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 65.0 µm/m-°C

@Temperature 20.0 °C
36.1 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Vicat Softening Point 135 °C
275 °F
Flammability, UL94 V-0

@Thickness 3.10 mm
V-0

@Thickness 0.122 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.7

@Frequency 100 Hz
2.7

@Frequency 100 Hz
2.8

@Frequency 1e+6 Hz
2.8

@Frequency 1e+6 Hz
Dielectric Strength 90.0 kV/mm
2290 kV/in
Dissipation Factor 0.0040

@Frequency 1e+6 Hz
0.0040

@Frequency 1e+6 Hz
Comparative Tracking Index 300 V
300 V