BASF Luranyl® KR 2450/3 Polyphenylene Ether + Styrene-Butadiene Blend

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend , Styrene-Butadiene
Manufacturer	BASF
Trade Name	Luranyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Luranyl® KR 2450/3 Polyphenylene Ether + Styrene-Butadiene Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Easy-flowing grade containing halogen-free, flame-retardant. Uses include: housings for electrical appliances, tubular wiring conduits, tachograph housings.Data was collected by ISO methods and provided by BASF.

Physical Properties	Metric	English
Density	1.10 g/cc	0.0397 lb/in³
Water Absorption	0.40 %	0.40 %
Moisture Absorption at Equilibrium	0.15 %	0.15 %
Linear Mold Shrinkage, Flow	0.0060 cm/cm	0.0060 in/in
High Load Melt Index	130 g/10 min @Load 21.6 kg, Temperature 250 °C	130 g/10 min @Load 47.6 lb, Temperature 482 °F

Mechanical Properties	Metric	English
Tensile Strength, Yield	60.0 MPa	8700 psi
Elongation at Break	45 %	45 %
Elongation at Yield	6.0 %	6.0 %
Tensile Modulus	2.50 GPa	363 ksi
Charpy Impact Unnotched	NB	NB
	2.00 J/cm² @Temperature -30.0 °C	9.52 ft-lb/in² @Temperature -22.0 °F
Charpy Impact, Notched	2.00 J/cm²	9.52 ft-lb/in²
	2.00 J/cm² @Temperature -30.0 °C	9.52 ft-lb/in² @Temperature -22.0 °F
Tensile Creep Modulus, 1000 hours	1850 MPa	268000 psi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	65.0 µm/m-°C @Temperature 20.0 °C	36.1 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	110 °C	230 °F
Deflection Temperature at 1.8 MPa (264 psi)	103 °C	217 °F
Vicat Softening Point	111 °C	232 °F
Flammability, UL94	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	37 %	37 %

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.8 @Frequency 100 Hz	2.8 @Frequency 100 Hz
	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz
Dielectric Strength	90.0 kV/mm	2290 kV/in
Dissipation Factor	0.0060 @Frequency 1e+6 Hz	0.0060 @Frequency 1e+6 Hz
Comparative Tracking Index	250 V	250 V