BASF Luranyl® KR 2403 G6 Polyphenylene Ether + Styrene-Butadiene Blend, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled , Styrene-Butadiene
Manufacturer BASF
Trade Name Luranyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Luranyl® KR 2403 G6 Polyphenylene Ether + Styrene-Butadiene Blend, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General-purpose grade with 30% glass fiber for parts requiring especially good resistance to heat deformation.Applications: parts for hot-water contact, pump housings, fan blades.Data was collected by ISO methods and provided by BASF.
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
Water Absorption 0.30 %
0.30 %
Moisture Absorption at Equilibrium 0.10 %
0.10 %
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
High Load Melt Index 7.0 g/10 min

@Load 21.6 kg,
Temperature 250 °C
7.0 g/10 min

@Load 47.6 lb,
Temperature 482 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 110 MPa
16000 psi
Elongation at Break 2.5 %
2.5 %
Tensile Modulus 9.00 GPa
1310 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
1.40 J/cm²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
Tensile Creep Modulus, 1 hour 7100 MPa
1.03e+6 psi
Tensile Creep Modulus, 1000 hours 6100 MPa
885000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C

@Temperature 20.0 °C
19.4 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Vicat Softening Point 145 °C
293 °F
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.9

@Frequency 100 Hz
2.9

@Frequency 100 Hz
2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
Dielectric Strength 90.0 kV/mm
2290 kV/in
Dissipation Factor 0.0010

@Frequency 1e+6 Hz
0.0010

@Frequency 1e+6 Hz
Comparative Tracking Index 250 V
250 V