BASF Capron® GR630 HS 30% Glass-Filled Nylon 66 (Conditioned)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® GR630 HS 30% Glass-Filled Nylon 66 (Conditioned)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron GR630 HS is a heat stabilized, 30% glass fiber reinforced polyamide 6,6 injection molding compound offering excellent strength, stiffness, creep resistance and dimensional stability. This balance of engineering properties combined with excellent processability make it ideal in applications replacing metal, resulting in overall cost and weight reduction. It is also available in non-heat stabilized (Capron GR630) and/or pigmented versions.Capron GR630 HS is generally recommended for switch components, valve bodies and relay parts.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 290-315 degC (555-600 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95degC (176-203 degF) is recommended, but temperatures of as low as 45 degC (113degF) and as high as 105 degC (221 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
(Dry)
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data MD (Dry)
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO Data (Dry)
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
(Dry)
Processing Properties Metric English Comments
Processing Temperature 290 °C
554 °F
See Materials Notes
Mold Temperature 80.0 °C
176 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes