BASF Capron® GR30 HS 30% Glass-Filled Nylon 6 (Conditioned)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® GR30 HS 30% Glass-Filled Nylon 6 (Conditioned)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron GR30 HS is a heat stabilized 30% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics. It is also available in non-heat stabilized (Capron GR30) and/or pigmented versions.Capron GR30 HS is generally recommended for applications such as chain saw, power tool housings, weed trimmer components, gears, automotive window hardware, under hood applications including cables, fittings, cooling fans, electrical connectors and coil bobbins.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 270-295 degC (518-563 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
(Dry)
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data MD (Dry)
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO Data (Dry)
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 115 MPa
16700 psi
ASTM data at 5 mm/min.
Tensile Strength, Yield 107 MPa
15500 psi
ISO value at 50 mm/min.
110 MPa
16000 psi
ASTM value at 50 mm/min.
Elongation at Break 6.0 %
6.0 %
Nominal
6.0 %
6.0 %
ASTM, 5 mm/minl
Elongation at Yield 5.9 %
5.9 %
ISO Value at 50 mm/min.
6.0 %
6.0 %
ASTM Value at 50 mm/min.
Tensile Modulus 4.92 GPa
714 ksi
same value from ASTM and ISO test.
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
(Dry)
Processing Properties Metric English Comments
Processing Temperature 275 °C
527 °F
See Materials Notes
Mold Temperature 95.0 °C
203 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes