BASF Capron® B73ZP Nylon 6 (DAM) (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Capron® B73ZP Nylon 6 (DAM)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % | 1.6 % | 24 hr.; ISO 62 |
| 9.5 % | 9.5 % | ISO 62 | |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 |
| Oxygen Transmission Rate | 40.3 cc/m²/day | 2.60 cc/100 in²/day | |
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | cc/m2/day (Thickness not reported) |
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | cc/m2/day (Thickness not reported) |
| Viscosity Measurement | 3.0 | 3.0 | Relative Viscosity (96% SAV) |
| 3.1 | 3.1 | Relative Viscosity (95% SAV) | |
| 3.2 | 3.2 | Relative Viscosity (98% SAV) | |
| 73 | 73 | Formic Acid; ASTM D789 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
| 80.0 MPa | 11600 psi | 2 in/min; ASTM D638 | |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 2.62 GPa | 380 ksi | ASTM D790 |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM D3418 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Unfilled | |
| Color | Natural | |
| Commercial Status (March 2007) | Active America | |
| FDA | 21 CFR 177.1500 | |
| Film Extrusion | Processable | |
| Impact Modified | No | |
| Injection molding | Processable | |
| Primary Processing Technique | Film Extrusion |
Users viewing this material also viewed the following:
- MV Labs Y870 Y2(C2O4)3·9H2O Yttrium oxalate hydrate
- Huntsman Araldite GT 6084 Bisphenol A Epoxy Solid Resin
- Techmer ES Electrafil® J-4/25/CF/15 NAT PA6/12
- SABIC Innovative Plastics LNP THERMOCOMP PF008 PA 6 (Asia Pacific)
- Wellman Wellamid® MRGF25/25 22H-GY1 Nylon 66, 25% Mineral and 25% Glass Reinforced
- DuPont™ Fusabond® C250 Polymer Modifier
- CLAL-MSX NICLAFOR® 1000 TB Quenched Rolled Copper Alloy
- ACC EP RP EPI Engineered Polymers Aromatic Polyurea
- ConocoPhillips Hydroclear® 100 3 EP gear Oil
Copyright © lookpolymers.com All Rights Reserved