BASF Capron® 8362 HS Impact Modified, 34% Mineral-Filled Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Mineral Reinforced, Impact Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8362 HS Impact Modified, 34% Mineral-Filled Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8362 HS is a 34% glass reinforced, impact modified, heat stabilized nylon6 injection molding compound exhibiting a high level of toughness in combination with excellent processability and surface aesthetics. It possesses excellent balance of strength and stiffness combined with a high level of drop weight impact as well as chemical resistance to greases, oils and hydrocarbons.Capron 8362 HS is generally recommended for applications such as wheel covers and hubs, mirror housings, appliance components and power tool housings.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 270-300 degC (518-572 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.109 g/cc
0.04007 lb/in³
Melt Density
1.43 g/cc
0.0517 lb/in³
ISO data
Moisture Absorption at Equilibrium 1.6 %
1.6 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 5.8 %
5.8 %
in water; 23°C; ISO data
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM Data MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 75.0 MPa
10900 psi
ASTM value at 50 mm/min.
76.0 MPa
11000 psi
ISO value at 50 mm/min.
Elongation at Break 17 %
17 %
Nominal
20 %
20 %
Nominal
Flexural Yield Strength 120 MPa
17400 psi
ASTM Data
Flexural Modulus 4.00 GPa
580 ksi
ISO Value
4.485 GPa
650.5 ksi
ASTM Value
Poissons Ratio 0.35
0.35
ISO data
Thermal Properties Metric English Comments
Specific Heat Capacity 2.77 J/g-°C
0.662 BTU/lb-°F
Melt value
Thermal Conductivity 0.234 W/m-K
1.62 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
ASTM Data
Processing Properties Metric English Comments
Drying Temperature 85.0 °C
185 °F
See Materials Notes