BASF Capron® 8333G HI HS BK-102 Impact Modified, 33% Glass-Filled Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8333G HI HS BK-102 Impact Modified, 33% Glass-Filled Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8333G HI HS BK-102 is a 33% glass reinforced, impact modified polyamide 6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics.Capron 8333G HI HS BK-102 is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware.Data provided by Allied Signal.Processing: Max. water content 0.12%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 270-295 degC (518-563 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) This product can be processed over a wide range of mold temperatures; however, for applications where aesthetics critical, a mold surface temperature of 80-95 degC (176-203 degF) is required. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Back pressure can be utilized to provide uniform melt consistency and reduce trapped air and gas. A maximum of 3.5 bar (50 psi) is recommended to minimize glass fiber breakage. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ISO data
Water Absorption 0.90 %
0.90 %
24 hrs; ISO data
Moisture Absorption at Equilibrium 1.5 %
1.5 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 5.5 %
5.5 %
in water; 23°C; ISO data
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 150 MPa
21800 psi
ASTM data at 5 mm/min.
152 MPa
22000 psi
ISO value at 5mm/min.
Elongation at Break 3.0 %
3.0 %
ISO, 5 mm/minl
3.0 %
3.0 %
ASTM, 5 mm/minl
Tensile Modulus 9.86 GPa
1430 ksi
same value from ASTM and ISO test.
Flexural Yield Strength 240 MPa
34800 psi
ASTM Data
Flexural Modulus 7.425 GPa
1077 ksi
ISO Value
8.14 GPa
1180 ksi
ASTM Value
Poissons Ratio 0.35
0.35
ISO data
Shear Modulus 3.70 GPa
537 ksi
calculated
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
ISO Data
1.10 J/cm²

@Temperature -30.0 °C
5.24 ft-lb/in²

@Temperature -22.0 °F
ISO data
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
ISO data
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO data
210 °C
410 °F
ASTM Data
Flammability, UL94 HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Drying Temperature 85.0 °C
185 °F
See Materials Notes