BASF Capron® 8203C Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8203C Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8203C is a high viscosity, nylon 6 extrusion compound, possessing a modified crystalline structure for increased property performance and faster set up for tubing and cable applications. It has high strength, stiffness and heat distortion temperature. It maintains excellent chemical resistance to greases, oils and hydrocarbons. It is available in natural, heat stabilized and pigmented versions.Capron 8203C is generally recommended for applications such as automotive tubing and cable liners. ASTM Callout PA234.Data provided by Allied Signal.Processing: Max. water content 0.25%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 240-280 degC (464-536 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95 degC (176-203 degF) is recommended, but temperatures of as low as 10 degC (50 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO data
Water Absorption 1.6 %
1.6 %
24 hrs; ISO data
Moisture Absorption at Equilibrium 2.6 %
2.6 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 9.3 %
9.3 %
in water; 23°C; ISO data
Viscosity Measurement 130
130
Formic Acid Viscosity; ISO data
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM Data MD
Mechanical Properties Metric English Comments
Tensile Strength, Yield 85.0 MPa
12300 psi
ASTM value at 50 mm/min.
86.0 MPa
12500 psi
ISO value at 50 mm/min.
Elongation at Break 20 %
20 %
Nominal
40 %
40 %
Nominal
Elongation at Yield 5.0 %
5.0 %
ISO Value at 50 mm/min.
5.0 %
5.0 %
ASTM Value at 50 mm/min.
Flexural Yield Strength 120 MPa
17400 psi
ASTM Data
Flexural Modulus 2.80 GPa
406 ksi
ISO Value
3.345 GPa
485.2 ksi
ASTM Value
Poissons Ratio 0.35
0.35
ISO data
Thermal Properties Metric English Comments
CTE, linear 81.0 µm/m-°C

@Temperature 20.0 °C
45.0 µin/in-°F

@Temperature 68.0 °F
ASTM data
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 0.46 MPa (66 psi) 198 °C
388 °F
ASTM Data
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ASTM Data
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 80.0 - 95.0 °C
176 - 203 °F
temperatures as low as 10°C (50°F) can be used where applicable.
Drying Temperature 85.0 °C
185 °F
See Materials Notes
Injection Pressure 3.45 - 10.3 MPa
500 - 1500 psi