BASF Capron® 1943 Impact Modified Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 1943 Impact Modified Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 1943 is a type 6 nylon graft copolymer developed for injection molding applications requiring improved dry as molded toughness, and increased flexibility. It has an excellent thermal and chemical properties provided with the polyamide backbone.Capron 1943 is generally recommended for applications such as cellular phone housings, handheld device, caps, furniture rails, escutcheons, covers, mower decks and tool.Data provided by Allied Signal.Processing: Max. water content 0.25%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 240-280 degC (464-536 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95 degC (176-203 degF) is recommended, but temperatures of as low as 10 degC (50 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 0.938 g/cc
0.0339 lb/in³
Melt Density
1.10 g/cc
0.0397 lb/in³
ISO data
Moisture Absorption at Equilibrium 2.4 %
2.4 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 8.6 %
8.6 %
in water; 23°C; ISO data
Mechanical Properties Metric English Comments
Tensile Strength, Yield 69.0 MPa
10000 psi
ISO value at 50 mm/min.
70.0 MPa
10200 psi
ASTM value at 50 mm/min.
Elongation at Break >= 50 %
>= 50 %
Nominal
70 %
70 %
Nominal
Flexural Yield Strength 95.0 MPa
13800 psi
ASTM Data
Flexural Modulus 2.39 GPa
347 ksi
ASTM Data
Poissons Ratio 0.35
0.35
ISO data
Thermal Properties Metric English Comments
Specific Heat Capacity 3.89 J/g-°C
0.930 BTU/lb-°F
Melt value
Thermal Conductivity 0.168 W/m-K
1.17 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ASTM Data
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Drying Temperature 85.0 °C
185 °F
See Materials Notes