BASF Capron® 1202CQ Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 1202CQ Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 1202CQ is a blended low viscosity, polyamide 6 injection molding homopolymer, possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in pigmented versions.Capron 1202CQ is generally recommended for applications such as furniture casters, gears, window hardware, end fittings, insulators, bushings, slides, valves, relays, wiring devices, and other electrical components.Data provided by Allied Signal.Processing: Max. water content 0.25%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 240-280 degC (464-536 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95 degC (176-203 degF) is recommended, but temperatures of as low as 10 degC (50 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO data
Water Absorption 1.6 %
1.6 %
24 hrs; ISO data
Moisture Absorption at Equilibrium 2.6 %
2.6 %
Water Absorption at Saturation 9.3 %
9.3 %
Viscosity Measurement 48
48
Formic Acid Viscosity; ISO data
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
ASTM data MD
0.013 cm/cm
0.013 in/in
ISO data
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO Data
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 75.0 MPa
10900 psi
ASTM data at 5 mm/min.
Tensile Strength, Yield 90.0 MPa
13100 psi
50 mm/min; Same value from ASTM and ISO test.
Elongation at Break 10 %
10 %
ASTM, 5 mm/minl
10 %
10 %
Nominal
Elongation at Yield 4.0 %
4.0 %
ISO Value at 50 mm/min.
4.0 %
4.0 %
ASTM Value at 50 mm/min.
Tensile Modulus 3.50 GPa
508 ksi
same value from ASTM and ISO test.
Flexural Yield Strength 130 MPa
18900 psi
ASTM Data
Flexural Modulus 3.17 GPa
460 ksi
ASTM Value
3.20 GPa
464 ksi
ISO Value
Poissons Ratio 0.35
0.35
ISO data
Shear Modulus 1.30 GPa
189 ksi
calculated
Thermal Properties Metric English Comments
CTE, linear 81.0 µm/m-°C

@Temperature 20.0 °C
45.0 µin/in-°F

@Temperature 68.0 °F
ASTM data
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
ISO data
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ISO Data
Processing Properties Metric English Comments
Processing Temperature 260 °C
500 °F
See Materials Notes
Mold Temperature 80.0 °C
176 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes