Azoty Tarnow™ Tarnamid® T-27 CFHI Polyamide 6 - Antistatic and Electroconductive

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name Tarnamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ Tarnamid® T-27 CFHI Polyamide 6 - Antistatic and Electroconductive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffness and strength.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration damping capacityGood fatigue strengthVery good sliding properties, abrasion resistance, low coefficient of frictionHigh thermal resistance, admissible temperature of continuous operation from -60°C to +150°CHigh chemical resistance, particularly to organic solvents, oils, lubricants and fuelsConsiderable moisture absorption influencing mechanical and electrical propertiesSelf-extinguishing properties (fire retardant properties)Good electro-insulating propertiesGood optical properties, relatively good transparency of molded pieces with thickness below 3.2 mm made from natural Tarnamid® (not dyed and not compounded)Can be used for the production of goods coming into contact with food (grades fulfilling requirement of European Union Directive No 2002/72/EEC) with latest amendmentsInformation provided by Azoty Tarnow™.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.011 cm/cm
0.011 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4
Melt Flow 35 g/10 min

@Load 5.00 kg,
Temperature 275 °C
35 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 90.0 MPa

@Load 36.5 kg
13100 psi

@Load 80.5 lb
cond.; ISO 2039-1
120 MPa

@Load 36.5 kg
17400 psi

@Load 80.5 lb
dry; ISO 2039-1
Tensile Strength 70.0 MPa
10200 psi
cond.; ISO 527
90.0 MPa
13100 psi
dry; ISO 527
Elongation at Break 6.0 %
6.0 %
dry; ISO 527
13 %
13 %
cond.; ISO 527
Tensile Modulus 4.00 GPa
580 ksi
cond.; ISO 527
5.50 GPa
798 ksi
dry; ISO 527
Flexural Strength <= 75.0 MPa
<= 10900 psi
cond.; ISO 178
<= 100 MPa
<= 14500 psi
dry; ISO 178
Charpy Impact Unnotched 8.00 J/cm²
38.1 ft-lb/in²
dry; ISO 179 1eU
11.0 J/cm²
52.3 ft-lb/in²
cond.; ISO 179 1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
dry; ISO 179 1eA
1.50 J/cm²
7.14 ft-lb/in²
cond.; ISO 179 1eA
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
dry; ISO 75
170 °C
338 °F
cond.; ISO 75
Vicat Softening Point 165 °C

@Load 5.10 kg
329 °F

@Load 11.2 lb
cond.; ISO 306
180 °C

@Load 5.10 kg
356 °F

@Load 11.2 lb
dry; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Surface Resistance 30 ohm
30 ohm
IEC 93
Processing Properties Metric English Comments
Melt Temperature 230 - 290 °C
446 - 554 °F
Mold Temperature 60.0 - 120 °C
140 - 248 °F
80 - 90°C is recommended
Drying Temperature 75.0 - 100 °C

@Time 7200 - 14400 sec
167 - 212 °F

@Time 2.00 - 4.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Injection Pressure 80.0 - 130 MPa
11600 - 18900 psi
80 MPa is recommended