Azoty Tarnow™ Tarnamid® T-27 CF20 Polyamide 6 20% Carbon Fiber- Antistatic and Electroconductive

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name Tarnamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ Tarnamid® T-27 CF20 Polyamide 6 20% Carbon Fiber- Antistatic and Electroconductive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffness and strength.Tarnamid® has the following main properties:High mechanical strength, rigidity and hardnessHigh impact strengthHigh vibration damping capacityGood fatigue strengthVery good sliding properties, abrasion resistance, low coefficient of frictionHigh thermal resistance, admissible temperature of continuous operation from -60°C to +150°CHigh chemical resistance, particularly to organic solvents, oils, lubricants and fuelsConsiderable moisture absorption influencing mechanical and electrical propertiesSelf-extinguishing properties (fire retardant properties)Good electro-insulating propertiesGood optical properties, relatively good transparency of molded pieces with thickness below 3.2 mm made from natural Tarnamid® (not dyed and not compounded)Can be used for the production of goods coming into contact with food (grades fulfilling requirement of European Union Directive No 2002/72/EEC) with latest amendmentsInformation provided by Azoty Tarnow™.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ISO 1183
Melt Flow 40 g/10 min

@Load 5.00 kg,
Temperature 275 °C
40 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 210 MPa

@Load 36.5 kg
30500 psi

@Load 80.5 lb
ISO 2039-1
Tensile Strength 175 MPa
25400 psi
ISO 527
Elongation at Break 4.0 %
4.0 %
ISO 527
Tensile Modulus 14.2 GPa
2060 ksi
ISO 527
Flexural Strength <= 240 MPa
<= 34800 psi
ISO 178
Charpy Impact Unnotched 5.20 J/cm²
24.7 ft-lb/in²
ISO 179 1eU
Charpy Impact, Notched 0.650 J/cm²
3.09 ft-lb/in²
ISO 179 1eA
Thermal Properties Metric English Comments
Melting Point 221 °C
430 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75
Vicat Softening Point 215 °C

@Load 5.10 kg
419 °F

@Load 11.2 lb
ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Surface Resistance 1.51 ohm
1.51 ohm
IEC 93
Processing Properties Metric English Comments
Melt Temperature 230 - 290 °C
446 - 554 °F
Mold Temperature 60.0 - 120 °C
140 - 248 °F
80 - 90°C is recommended
Drying Temperature 75.0 - 100 °C

@Time 7200 - 14400 sec
167 - 212 °F

@Time 2.00 - 4.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Injection Pressure 80.0 - 130 MPa
11600 - 18900 psi
80 MPa is recommended