Azoty Tarnow™ TARNOFORM 300 XEC1 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARNOFORM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARNOFORM 300 XEC1 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Electrically conductive, carbon fiber reinforced injection molding grade suitable for the applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Density 1.423 g/cc
0.05141 lb/in³
ISO 1183
Water Absorption 0.23 %
0.23 %
ISO 62
Linear Mold Shrinkage 0.0234 cm/cm

@Thickness 4.00 mm
0.0234 in/in

@Thickness 0.157 in
Melt Flow 11.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
11.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 176 MPa
25500 psi
358 N; ISO 2039-1
Tensile Strength, Yield 86.0 MPa
12500 psi
ISO 527
Elongation at Break 25 %
25 %
ISO 527
Tensile Modulus 5.60 GPa
812 ksi
ISO 527
Flexural Strength 110 MPa
16000 psi
ISO 178
Izod Impact, Notched (ISO) 6.50 kJ/m²
3.09 ft-lb/in²
1A; ISO 180
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
Melting Point 167 °C
333 °F
10°C/min.; ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 137 °C
279 °F
ISO 75
Vicat Softening Point 155 °C
311 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1e+05
1e+05
IEC 60093
Surface Resistance 1000 ohm
1000 ohm
IEC 60093
Processing Properties Metric English Comments
Processing Temperature 180 - 230 °C
356 - 446 °F
Barrel temperature
Mold Temperature 60.0 - 120 °C
140 - 248 °F