Azoty Tarnow™ TARNOFORM 300 TF2 POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled
Manufacturer	Azoty Tarnow™ (Zaklady Azotowe)
Trade Name	TARNOFORM
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Azoty Tarnow™ TARNOFORM 300 TF2 POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Tribological modified grade with addition of 10% PTFE, which causes decreased coefficient of friction and wear.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.

Physical Properties	Metric	English	Comments
Density	1.46 g/cc	0.0527 lb/in³	ISO 1183
Melt Flow	8.5 g/10 min @Load 2.16 kg, Temperature 190 °C	8.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	55.0 MPa	7980 psi	ISO 527
Elongation at Break	33 %	33 %	ISO 527
Flexural Strength	57.0 MPa	8270 psi	ISO 178
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	1eA; ISO 179

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	1.48 J/g-°C	0.354 BTU/lb-°F
Melting Point	167 °C	333 °F	10°C/min.; ISO 3146
Deflection Temperature at 1.8 MPa (264 psi)	112 °C	234 °F	ISO 75
Vicat Softening Point	151 °C	304 °F	50 N; ISO 306
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	3.8 @Frequency 1e+6 Hz	3.8 @Frequency 1e+6 Hz	IEC 60250
Dielectric Strength	24.0 kV/mm	610 kV/in	IEC 60243
Dissipation Factor	0.010 @Frequency 1e+6 Hz	0.010 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 112

Processing Properties	Metric	English	Comments
Processing Temperature	180 - 230 °C	356 - 446 °F	Barrel temperature
Mold Temperature	60.0 - 120 °C	140 - 248 °F

Users viewing this material also viewed the following: