Azoty Tarnow™ TARNOFORM 300 GF2 GB2 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARNOFORM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARNOFORM 300 GF2 GB2 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% glass fiber/10% glass beads mix reinforced injection molding grade, suitable for applications where increased strength and stiffness is required with care of the surface quality.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Water Absorption 0.24 %
0.24 %
ISO 62
Melt Flow 8.73 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.73 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 211 MPa
30600 psi
358 N; ISO 2039-1
Tensile Strength, Yield 74.0 MPa
10700 psi
ISO 527
Elongation at Break 2.5 %
2.5 %
ISO 527
Tensile Modulus 5.20 GPa
754 ksi
ISO 527
Flexural Strength 107 MPa
15500 psi
ISO 178
Izod Impact, Notched (ISO) 4.80 kJ/m²
2.28 ft-lb/in²
1A; ISO 180
Charpy Impact, Notched 0.360 J/cm²
1.71 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
Melting Point 167 °C
333 °F
10°C/min.; ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 159 °C
318 °F
ISO 75
Vicat Softening Point 157 °C
315 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 4.0

@Frequency 100 Hz
4.0

@Frequency 100 Hz
IEC 60250
4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243
Dissipation Factor 0.0095

@Frequency 1e+6 Hz
0.0095

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Processing Temperature 180 - 230 °C
356 - 446 °F
Barrel temperature
Mold Temperature 60.0 - 120 °C
140 - 248 °F