Azoty Tarnow™ TARNOFORM 200 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARNOFORM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARNOFORM 200 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This material is a standard extrusion grade, also could be used for injection molding of low shape complexity details.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Linear Mold Shrinkage 0.030 cm/cm

@Thickness 4.00 mm
0.030 in/in

@Thickness 0.157 in
Melt Flow 2.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ISO 2039-2
Ball Indentation Hardness 135 MPa
19600 psi
358 N; ISO 2039-1
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527
Elongation at Break 65 %
65 %
ISO 527
Flexural Strength 57.0 MPa
8270 psi
ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
1A; ISO 180
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
Specific Heat Capacity 1.48 J/g-°C
0.354 BTU/lb-°F
Melting Point 167 °C
333 °F
10°C/min.; ISO 3146
Maximum Service Temperature, Air 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
ISO 75
Vicat Softening Point 150 °C
302 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
IEC 60093
Dielectric Constant 3.9

@Frequency 1e+6 Hz
3.9

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 25.0 kV/mm
635 kV/in
IEC 60243
Dissipation Factor 0.0085

@Frequency 1e+6 Hz
0.0085

@Frequency 1e+6 Hz
IEC 60250
Arc Resistance 1.9 sec
1.9 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Processing Temperature 180 - 210 °C
356 - 410 °F
Barrel temperature
Mold Temperature 60.0 - 120 °C
140 - 248 °F