Azdel AZMET® CM20350 35% continuous random fiber mat / PBT resin matrix

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Azdel
Trade Name AZMET®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azdel AZMET® CM20350 35% continuous random fiber mat / PBT resin matrix.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AZDEL® CM20350 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a Polybutylene Terephthalate (PBT) resin matrix. This composite material features high flow properties and a generally homogeneous fiber distribution. This material is typically used for standard semi-structural applications where high stiffness and impact are desired.Mechanical properties and mold shrinkage measured on flat plaques.Information provided by Azdel.
Physical Properties Metric English Comments
Specific Gravity 1.59 g/cc
1.59 g/cc
Laminate; ASTM D792
1.62 g/cc
1.62 g/cc
Molded; ASTM D792
Filler Content 35 %
35 %
By weight (ashing); Internal
Thickness 3350 microns
132 mil
Sheet; Internal
Linear Mold Shrinkage 0.0030 - 0.0040 cm/cm
0.0030 - 0.0040 in/in
Measured on flat plaques; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 104 MPa
15100 psi
ISO 527
Elongation at Break 2.0 %
2.0 %
ISO 527
Tensile Modulus 8.28 GPa
1200 ksi
ISO 527
Flexural Strength 220 MPa
31900 psi
ISO 178
Flexural Modulus 8.28 GPa
1200 ksi
ISO 178
Poissons Ratio 0.32
0.32
ISO 527
Izod Impact, Notched 6.94 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
13.0 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Impact Test 29.0 J

@Thickness 4.00 mm
21.4 ft-lb

@Thickness 0.157 in
Multi-axial, at failure; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 218 °C
424 °F
ASTM D648
Descriptive Properties Value Comments
Color Black
Internal