Axiall SP-6655 Rigid PVC, Molding
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | Axiall |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Axiall SP-6655 Rigid PVC, Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Georgia Gulf SP-6655 is a high flow rigid PVC compound designed for electrical and custom molding applications. This compound features excellent physical properties, good melt flow, and exceptionally high impact strength, especially at low temperatures. SP-6655 UL Flammability rating and elevated UL Relative Thermal Index rating are provided.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | Natural; ASTM D-792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D-955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 37.9 MPa | 5500 psi | ASTM D-638 |
| Tensile Modulus | 2.28 GPa | 330 ksi | ASTM D-638 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D-256 |
| 1.07 J/cm @Thickness 3.17 mm, Temperature -20.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature -4.00 °F |
ASTM D-256 | |
| 5.34 J/cm @Thickness 3.17 mm, Temperature 0.000 °C |
10.0 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
ASTM D-256 | |
| 6.94 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
13.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D-256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 68.00 °C | 154.4 °F | unannealed; ASTM D-648 |
| 75.0 °C | 167 °F | annealed; ASTM D-648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.00 °C | 141.8 °F | unannealed; ASTM D-648 |
| 69.00 °C | 156.2 °F | annealed; ASTM D-648 | |
| Vicat Softening Point | 88.3 °C | 191 °F | annealed; ASTM D-1525A |
| UL RTI, Electrical | 95.0 °C | 203 °F | UL-746B |
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL-746B |
| UL RTI, Mechanical without Impact | 85.0 °C | 185 °F | UL-746B |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cell Classification | 14002123 | ASTM D-4216 |
| Cell Classification, ASTM D-1784 | 15233 |