Axiall CL-6400 Rigid PVC, Molding

Category	Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer	Axiall
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Axiall CL-6400 Rigid PVC, Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Georgia Gulf CL-6400 is a high flow clear PVC compound designed for thin wall parts and multi-cavity molds. It is ideally suited for a variety of electrical and appliance applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.

Physical Properties	Metric	English	Comments
Specific Gravity	1.40 g/cc	1.40 g/cc	ASTM D-792
Linear Mold Shrinkage	0.0030 - 0.0040 cm/cm	0.0030 - 0.0040 in/in	ASTM D-955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	44.8 MPa	6500 psi	ASTM D-638
Tensile Modulus	2.76 GPa	400 ksi	ASTM D-638
Flexural Strength	75.8 MPa	11000 psi	ASTM D-790
Flexural Modulus	2.41 GPa	350 ksi	ASTM D-790
Izod Impact, Notched	4.27 J/cm @Thickness 3.17 mm, Temperature 23.0 °C	8.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	ASTM D-256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	71.00 °C	159.8 °F	annealed; ASTM D-648
Deflection Temperature at 1.8 MPa (264 psi)	69.00 °C	156.2 °F	annealed; ASTM D-648
UL RTI, Electrical	85.0 °C @Thickness 1.60 mm	185 °F @Thickness 0.0630 in	UL-746B
UL RTI, Mechanical with Impact	85.0 °C @Thickness 1.60 mm	185 °F @Thickness 0.0630 in	UL-746B
UL RTI, Mechanical without Impact	85.0 °C @Thickness 1.60 mm	185 °F @Thickness 0.0630 in	UL-746B
Flammability, UL94	V-0	V-0

Descriptive Properties	Value	Comments
Flow Ratio (Distance/Wall Thickness, 390-400°F)	230	Georgia Gulf Test