Assab Steels ASP 60 Cold Work Steel

Category Metal , Ferrous Metal , Tool Steel , Cold Work Steel
Manufacturer Assab Steels
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Assab Steels ASP 60 Cold Work Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ASP 60 is a W-Mo-V-Co alloyed PM high speed steel characterized by:Highest wear resistanceMaximum compressive strengthGood through hardening propertiesGood toughnessGood dimensional stability on heat treatmentVery good temper resistanceW.-Nr. 1.3241
Physical Properties Metric English Comments
Density 7.89 g/cc
0.285 lb/in³
soft annealed condition
7.78 g/cc

@Temperature 600 °C
 0.281 lb/in³

@Temperature 1110 °F
 soft annealed condition
7.83 g/cc

@Temperature 400 °C
 0.283 lb/in³

@Temperature 752 °F
 soft annealed condition
Mechanical Properties Metric English Comments
Hardness, Rockwell C 62
62
Final Hardness after tempering 3 times for one hour at 560°C (1040°F). Austenitizing temperature 960°C (1760°F). ±1 HRC
64
64
Final Hardness after tempering 3 times for one hour at 560°C (1040°F). Austenitizing temperature 1000°C (1832°F). ±1 HRC
66
66
Final Hardness after tempering 3 times for one hour at 560°C (1040°F). Austenitizing temperature 1070°C (1960°F). ±1 HRC
68
68
Final Hardness after tempering 3 times for one hour at 560°C (1040°F). Austenitizing temperature 1150°C (2102°F). ±1 HRC
69
69
Final Hardness after tempering 3 times for one hour at 560°C (1040°F). Austenitizing temperature 1180°C (2156°F). ±1 HRC
60.5

@Temperature 500 °C
 60.5

@Temperature 932 °F
 Hot Hardness. Austenitizing temperature: 1100°C (2010°F).
62

@Temperature 500 °C
 62

@Temperature 932 °F
 Hot Hardness. Austenitizing temperature: 1180°C (2160°F).
65.5

@Temperature 100 °C
 65.5

@Temperature 212 °F
 Hot Hardness. Austenitizing temperature: 1100°C (2010°F).
67

@Temperature 100 °C
 67

@Temperature 212 °F
 Hot Hardness. Austenitizing temperature: 1180°C (2160°F).
66

@Diameter 5.00 mm
 66

@Diameter 0.197 in
 Four point bend testing. 5mm/min. Austenitizing temperature: 1050°C Tempering: 3X1 h at 560°C, AC
68

@Diameter 5.00 mm
 68

@Diameter 0.197 in
 Four point bend testing. 5mm/min. Austenitizing temperature: 1050°C Tempering: 3X1 h at 560°C, AC
Modulus of Elasticity 250 GPa
36300 ksi
200 GPa

@Temperature 400 °C
 29000 ksi

@Temperature 752 °F
Flexural Strength 2500 MPa
363000 psi
3200 MPa
464000 psi
3500 MPa
508000 psi
3800 MPa
551000 psi
4500 MPa
653000 psi
Thermal Properties Metric English Comments
CTE, linear 10.6 µm/m-°C

@Temperature 20.0 - 400 °C
 5.89 µin/in-°F

@Temperature 68.0 - 752 °F
 for the hardened and tempered condition
11.1 µm/m-°C

@Temperature 20.0 - 600 °C
 6.17 µin/in-°F

@Temperature 68.0 - 1110 °F
 for the hardened and tempered condition
Specific Heat Capacity 0.418 J/g-°C

@Temperature 20.0 °C
 0.100 BTU/lb-°F

@Temperature 68.0 °F
 hardened and tempered condition
0.502 J/g-°C

@Temperature 400 °C
 0.120 BTU/lb-°F

@Temperature 752 °F
 hardened and tempered condition
0.586 J/g-°C

@Temperature 600 °C
 0.140 BTU/lb-°F

@Temperature 1110 °F
 hardened and tempered condition
Thermal Conductivity 21.0 W/m-K

@Temperature 20.0 °C
 146 BTU-in/hr-ft²-°F

@Temperature 68.0 °F
 hardened and tempered condition
24.0 W/m-K

@Temperature 600 °C
 167 BTU-in/hr-ft²-°F

@Temperature 1110 °F
 hardened and tempered condition
25.0 W/m-K

@Temperature 400 °C
 174 BTU-in/hr-ft²-°F

@Temperature 752 °F
 hardened and tempered condition
Component Elements Properties Metric English Comments
Carbon, C 2.3 %
2.3 %
Chromium, Cr 4.2 %
4.2 %
Cobalt, Co 10.5 %
10.5 %
Iron, Fe 63 %
63 %
Molybdenum, Mo 7.0 %
7.0 %
Tungsten, W 6.5 %
6.5 %
Vanadium, V 6.5 %
6.5 %