Ascend Performance Materials Vydyne® R540 Nylon 66, 40% Glass Reinforced, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R540 Nylon 66, 40% Glass Reinforced, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R540 is general-purpose, hydrolysis-resistant, 40% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solution at elevated temperatures. This product is also lubricated for improved flow and offers superior surface appearance. Glass-reinforced Vydyne resins provide higher hear distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents..Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 40% Filler by WeightAdditive:Lubricant Features: Antifreeze ResistantFatigue ResistantGasoline ResistanceGood Chemical ResistanceGood FlowHydrolysis ResistantLubricatedSolvent Resistant Appearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ISO 1183
Water Absorption 0.60 %

@Time 86400 sec
0.60 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.5 %
1.5 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Diameter 2.00 mm
0.0040 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Diameter 2.00 mm
0.0090 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 165 MPa
23900 psi
ISO 527-2
Elongation at Break 4.0 %
4.0 %
ISO 527-2
Tensile Modulus 11.1 GPa
1610 ksi
ISO 527-2
Flexural Strength 250 MPa
36300 psi
ISO 178
Flexural Modulus 9.30 GPa
1350 ksi
ISO 178
Izod Impact, Notched (ISO) 13.0 kJ/m²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
ISO 180
19.0 kJ/m²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 8.70 J/cm²

@Temperature -30.0 °C
41.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179
9.20 J/cm²

@Temperature 23.0 °C
43.8 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
ISO 179
1.90 J/cm²

@Temperature 23.0 °C
9.04 ft-lb/in²

@Temperature 73.4 °F
ISO 179