Ascend Performance Materials Vydyne® R513H Nylon 66, 13% Glass Filled, Conditioned (2.5% Moisture)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R513H Nylon 66, 13% Glass Filled, Conditioned (2.5% Moisture).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R513H is general-purpose, 13% glass-reinforced, heat stabilized PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow, and mold release. Glass-reinforced Vydyne resins provide a higher heat distortion temperature, better resistance to creep, higher impact, and better dimensional stability when compared with unreinforced PA66. This product has good chemical resistance to a broad range of chemicals, including many aliphatic and aromatic hydrocarbons found in most solvent, gasoline, hydraulic fluids, greases and machine oils. Vydyne R513 has tensile strength and modulus properties just below aluminum and zinc can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyen glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts. Vydyne R513H is heat-stabilized and formulated to minimize the oxidative and thermal degradation of the PA66 polymer when exposed to elevated temperature for extended periods of time. Vydyne R513H provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275°F, with short-term peak temperature as high as 475°F. Typical Applications/End Uses: Vydyne R513H resin has been used for many under-th-hood automotive applications, motor housings for power tools and garden appliances. The resin has also been used in miscellaneous brackets, gears and clips, which require high rigidity and strength.Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 13% Filler by Weight Additive:Heat StabilizerLubricant Features: Gasoline ResistanceGood Chemical Resistance Good FlowGood Mold ReleaseGrease ResistantHeat Stabilized High RigidityHigh StrengthLubricatedOil ResistantSolvent ResistantUses: Automotive Under the Hood GearsHousings Power/Other ToolsAppearance: Natural ColorForms: PelletsProcessing Method: Injection Molding
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ISO 1183
Water Absorption 1.0 %

@Time 86400 sec
1.0 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
50% RH; ISO 62
Linear Mold Shrinkage 0.0050 cm/cm

@Thickness 2.00 mm
0.0050 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 2.00 mm
0.010 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527-2
75.0 MPa
10900 psi
ISO 527-2
Elongation at Break 13 %
13 %
ISO 527-2
Tensile Modulus 3.90 GPa
566 ksi
ISO 527-2
Flexural Strength 106 MPa
15400 psi
ISO 178
Flexural Modulus 3.15 GPa
457 ksi
ISO 178
Izod Impact, Notched (ISO) 5.40 kJ/m²

@Temperature -30.0 °C
2.57 ft-lb/in²

@Temperature -22.0 °F
ISO 180
8.50 kJ/m²

@Temperature 23.0 °C
4.04 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 3.70 J/cm²

@Temperature -30.0 °C
17.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179
4.20 J/cm²

@Temperature 23.0 °C
20.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.530 J/cm²

@Temperature -30.0 °C
2.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179
0.750 J/cm²

@Temperature 23.0 °C
3.57 ft-lb/in²

@Temperature 73.4 °F
ISO 179