Ascend Performance Materials Vydyne® R513H Black Nylon 66, 13% Glass Reinforced, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R513H Black Nylon 66, 13% Glass Reinforced, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R513H Black is general-purpose, 13% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is an injection-molding grade that is lubricated for machine feed, flow, and mold release. Glass-reinforced Vydyne resins provide a higher heat distortion temperature, better resistance to creep, high impact, and better dimensional stability when compared with unreinforced PA66. This product has good chemical resistance to a broad range of chemicals, including many aliphatic and aromatic hydrocarbons found in most solvents, gasoline, hydraulic fluids, greases and machine oils. Vydyne R513 Black has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts. Vydyne R513 Black is heat-stabilized and formulated to minimize the oxidative and thermal degradation of the PA66 polymer when exposed to elevated temperatures for extended periods of time. Vydyne R513H Black provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275°F, with short-term peak temperatures as high as 475°F. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 13% Filler by WeightAdditive:Heat StabilizerLubricant Features: Gasoline ResistanceGood Chemical ResistanceGood FlowGood Mold ReleaseGrease ResistantHeat StabilizedHigh RigidityHigh StrengthLubricatedOil ResistantSolvent ResistantUses: Automotive Under the Hood GearsHousings Power/Other ToolsAppearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.23 g/cc
0.0444 lb/in³
ISO 1183
Water Absorption 1.0 %

@Time 86400 sec
1.0 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.2 %
2.2 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0050 cm/cm

@Diameter 2.00 mm
0.0050 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Diameter 2.00 mm
0.010 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527-2
Elongation at Break 13 %
13 %
ISO 527-2
Tensile Modulus 3.90 GPa
566 ksi
ISO 527-2
Flexural Strength 106 MPa
15400 psi
ISO 178
Flexural Modulus 3.15 GPa
457 ksi
ISO 178
Izod Impact, Notched (ISO) 5.40 kJ/m²

@Temperature -30.0 °C
2.57 ft-lb/in²

@Temperature -22.0 °F
ISO 180
8.50 kJ/m²

@Temperature 23.0 °C
4.04 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 3.70 J/cm²

@Temperature -30.0 °C
17.6 ft-lb/in²

@Temperature -22.0 °F
ISO 179
4.20 J/cm²

@Temperature 23.0 °C
20.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.530 J/cm²

@Temperature -30.0 °C
2.52 ft-lb/in²

@Temperature -22.0 °F
ISO 179
0.750 J/cm²

@Temperature 23.0 °C
3.57 ft-lb/in²

@Temperature 73.4 °F
ISO 179