Ascend Performance Materials Vydyne® 65A Nylon 66, General Purpose, intermediate viscosity, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 65A Nylon 66, General Purpose, intermediate viscosity, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 65A is a medium-viscosity, heat-stabilized PA66 resin suitable for injection-molding extrusion and compounding applications. It is available in natural color only. Vydyne 65A resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles.Availability:Asia PacificEuropeNorth AmericaAdditive: Heat StabilizerSlip Features:General PurposeGood Chemical ResistanceGood ToughnessHeat StabilizedHigh RigidityHigh StrengthMedium ViscosityOil ResistantSolvent ResistantUses:Industrial ApplicationsMonofilamentsProfilesRodsSheetTubingAppearance: Natural ColorForms: PelletsProcessing Method: Extrusion and Injection MoldingInformation provided by Ascend
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ISO 1183
Water Absorption 8.5 %
8.5 %
24 hrs; ISO 62
Moisture Absorption at Equilibrium 2.5 %
2.5 %
Equilibrium at 50%rh; ISO 62
Linear Mold Shrinkage 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Thickness 2.00 mm
0.018 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
ISO 527-2
Tensile Strength, Yield 85.0 MPa
12300 psi
ISO 527-2
Elongation at Break >= 25 %
>= 25 %
ISO 527-2
Elongation at Yield 5.5 %
5.5 %
ISO 527-2
Tensile Modulus 3.10 GPa
450 ksi
ISO 527-2
Flexural Strength 75.0 MPa
10900 psi
ISO 178
Flexural Modulus 2.80 GPa
406 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75-2/A
Processing Properties Metric English Comments
Zone 1 250 - 295 °C
482 - 563 °F
Zone 2 250 - 295 °C
482 - 563 °F
Zone 3 250 - 295 °C
482 - 563 °F
Zone 4 250 - 295 °C
482 - 563 °F
Zone 5 250 - 295 °C
482 - 563 °F
Die Temperature 270 - 295 °C
518 - 563 °F
Melt Temperature 270 - 295 °C
518 - 563 °F
Back Pressure 3.00 - 17.0 MPa
435 - 2470 psi
Descriptive Properties Value Comments
Blown Film Bath Temperature 20-80°C
Chill Roll Temperature (Cast Film) 20-80°C