Ascend Performance Materials Vydyne® 49 Nylon 66, Impact Modified, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 49 Nylon 66, Impact Modified, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 49 is general-purpose, impact-modified PA66 resin. Available in natural, is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Typical Applications/End Uses: Vydyne 49 may be used in most market segments, including industrial, consumer, automotive and electrical applications. Typical end uses include clips, fasteners, gears, cable ties, electrical connectors and many other parts that require additional toughness at room and low temperatures. Availability:Asia PacificEuropeNorth AmericaAdditive:Impact Modifier Features: Gasoline ResistanceGeneral PurposeGood Abrasion ResistanceGood Chemical ResistanceGood ProcessabilityGood ToughnessHigh Impact ResistanceImpact ModifiedLow Temperature Impact ResistanceLow Temperature ToughnessOil ResistantSolvent ResistantUses:Automotive ApplicationsConnectorsConsumer ApplicationsElectrical/Electronic ApplicationsFastenersGearsIndustrial ApplicationsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Water Absorption 1.3 %

@Time 86400 sec
1.3 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Diameter 2.00 mm
0.018 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Diameter 2.00 mm
0.016 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
ISO 527-2
Tensile Strength, Yield 70.0 MPa
10200 psi
ISO 527-2
Elongation at Break 17 %
17 %
ISO 527-2
Tensile Modulus 3.04 GPa
441 ksi
ISO 527-2
Flexural Strength 81.0 MPa
11700 psi
ISO 178
Flexural Modulus 2.60 GPa
377 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
ISO 180
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
ISO 180
10.0 kJ/m²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.800 J/cm²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
ISO 179
1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
ISO 179
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 8.60 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
4.78 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
CTE, linear, Transverse to Flow 12.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
6.67 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 202 °C
396 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 69.0 °C
156 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 125 °C

@Thickness 0.750 mm
257 °F

@Thickness 0.0295 in
UL 746
125 °C

@Thickness 1.50 mm
257 °F

@Thickness 0.0591 in
UL 746
125 °C

@Thickness 3.00 mm
257 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.750 mm
167 °F

@Thickness 0.0295 in
UL 746
75.0 °C

@Thickness 1.50 mm
167 °F

@Thickness 0.0591 in
UL 746
75.0 °C

@Thickness 3.00 mm
167 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 0.750 mm
185 °F

@Thickness 0.0295 in
UL 746
85.0 °C

@Thickness 1.50 mm
185 °F

@Thickness 0.0591 in
UL 746
85.0 °C

@Thickness 3.00 mm
185 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Glow Wire Test 700 °C

@Thickness 0.750 mm
1290 °F

@Thickness 0.0295 in
Flammability Index; IEC 60695-2-12
700 °C

@Thickness 3.00 mm
1290 °F

@Thickness 0.118 in
Flammability Index; IEC 60695-2-12
725 °C

@Thickness 0.750 mm
1340 °F

@Thickness 0.0295 in
Ignition Temperature; IEC 60695-2-13
725 °C

@Thickness 3.00 mm
1340 °F

@Thickness 0.118 in
Ignition Temperature; IEC 60695-2-13
750 °C

@Thickness 1.50 mm
1380 °F

@Thickness 0.0591 in
Flammability Index; IEC 60695-2-12
775 °C

@Thickness 1.50 mm
1430 °F

@Thickness 0.0591 in
Ignition Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm

@Thickness 0.750 mm
1.00e+12 ohm-cm

@Thickness 0.0295 in
IEC 60093
Dielectric Strength 23.0 kV/mm

@Thickness 1.00 mm
584 kV/in

@Thickness 0.0394 in
IEC 60243
Arc Resistance 120 - 179 sec

@Thickness 3.00 mm
120 - 179 sec

@Thickness 0.118 in
ASTM D495
Comparative Tracking Index 600 V

@Thickness 3.00 mm
600 V

@Thickness 0.118 in
IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.750 mm
7.0 - 14 sec

@Thickness 0.0295 in
UL 746
7.0 - 14 sec

@Thickness 1.50 mm
7.0 - 14 sec

@Thickness 0.0591 in
UL 746
14 - 29 sec

@Thickness 3.00 mm
14 - 29 sec

@Thickness 0.118 in
UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
>= 120 arcs

@Thickness 0.0295 in
UL 746
>= 120 arcs

@Thickness 1.50 mm
>= 120 arcs

@Thickness 0.0591 in
UL 746
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
UL 746
High Voltage Arc-Tracking Rate, HVTR 10.1 - 25.4 mm/min
0.398 - 1.00 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 310 °C
536 - 590 °F
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Front Barrel Temperature 280 - 310 °C
536 - 590 °F
Nozzle Temperature 280 - 310 °C
536 - 590 °F
Melt Temperature 285 - 305 °C
545 - 581 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %
Users viewing this material also viewed the following: