Ascend Performance Materials Vydyne® 49 Nylon 66, Impact Modified, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 49 Nylon 66, Impact Modified, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 49 is general-purpose, impact-modified PA66 resin. Available in natural, is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Typical Applications/End Uses: Vydyne 49 may be used in most market segments, including industrial, consumer, automotive and electrical applications. Typical end uses include clips, fasteners, gears, cable ties, electrical connectors and many other parts that require additional toughness at room and low temperatures. Availability:Asia PacificEuropeNorth AmericaAdditive:Impact Modifier Features: Gasoline ResistanceGeneral PurposeGood Abrasion ResistanceGood Chemical ResistanceGood ProcessabilityGood ToughnessHigh Impact ResistanceImpact ModifiedLow Temperature Impact ResistanceLow Temperature ToughnessOil ResistantSolvent ResistantUses:Automotive ApplicationsConnectorsConsumer ApplicationsElectrical/Electronic ApplicationsFastenersGearsIndustrial ApplicationsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Water Absorption 1.3 %

@Time 86400 sec
1.3 %

@Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Diameter 2.00 mm
0.018 in/in

@Diameter 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Diameter 2.00 mm
0.016 in/in

@Diameter 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
ISO 527-2
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527-2
Elongation at Break 40 %
40 %
ISO 527-2
Tensile Modulus 2.13 GPa
309 ksi
ISO 527-2
Flexural Strength 27.0 MPa
3920 psi
ISO 178
Flexural Modulus 8.90 GPa
1290 ksi
ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -40.0 °C
4.76 ft-lb/in²

@Temperature -40.0 °F
ISO 180
15.0 kJ/m²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
ISO 180
37.0 kJ/m²

@Temperature 23.0 °C
17.6 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²

@Temperature -40.0 °C
2.86 ft-lb/in²

@Temperature -40.0 °F
ISO 179
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179
4.30 J/cm²

@Temperature 23.0 °C
20.5 ft-lb/in²

@Temperature 73.4 °F
ISO 179