Asahi Kasei Xyron® X9102 Modified Polyphenylene Ether

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer Asahi Kasei
Trade Name Xyron®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Xyron® X9102 Modified Polyphenylene Ether.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High-Heat ResistantInformation provided by Asahi Kasei
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
23°C; ASTM D792
Moisture Absorption 0.0600 %
0.0600 %
23°C, 50% RH 24 hours; ASTM D570
Linear Mold Shrinkage 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 64.0 MPa
9280 psi
23°C, 50% RH; ASTM D638
Elongation at Break 50 %
50 %
23°C, 50% RH; ASTM D638
Flexural Strength 83.0 MPa
12000 psi
23°C, 50% RH; ASTM D790
Flexural Modulus 2.16 GPa
313 ksi
23°C, 50% RH; ASTM D790
Izod Impact, Notched 0.780 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
1.46 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
0.980 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.84 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 65.0 µm/m-°C

@Temperature -30.0 - 60.0 °C
36.1 µin/in-°F

@Temperature -22.0 - 140 °F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
50% RH; ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
50% RH; ASTM D257
Dielectric Constant 2.8

@Frequency 1e+6 Hz
2.8

@Frequency 1e+6 Hz
50% RH; ASTM D150
2.8

@Frequency 1e+6 Hz
2.8

@Frequency 1e+6 Hz
50% RH; ASTM D150
Dielectric Strength 30.0 kV/mm

@Thickness 2.00 mm
762 kV/in

@Thickness 0.0787 in
Short time; ASTM D149
Dissipation Factor 0.00050

@Frequency 60 Hz
0.00050

@Frequency 60 Hz
50% RH; ASTM D150
0.00060

@Frequency 1e+6 Hz
0.00060

@Frequency 1e+6 Hz
50% RH; ASTM D150
Arc Resistance 80 sec
80 sec
Tungsten; ASTM D495
Processing Properties Metric English Comments
Processing Temperature 290 - 320 °C
554 - 608 °F
Resin Temperature
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Drying Temperature 90.0 - 100 °C
194 - 212 °F
Pre-drying Temperature
Dry Time 2 - 4 hour
2 - 4 hour