Asahi Kasei Xyron® A0100 PPE/PA

Category Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer Asahi Kasei
Trade Name Xyron®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Asahi Kasei Xyron® A0100 PPE/PA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AutomotiveInformation provided by Asahi Kasei
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
23°C; ASTM D792
Moisture Absorption 0.100 %
0.100 %
23°C, 50% RH 24 hours; ASTM D570
Linear Mold Shrinkage 0.011 - 0.014 cm/cm
0.011 - 0.014 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 49.0 MPa
7110 psi
23°C, 50% RH; ASTM D638
Elongation at Break 98 %
98 %
23°C, 50% RH; ASTM D638
Flexural Strength 74.0 MPa
10700 psi
23°C, 50% RH; ASTM D790
Flexural Modulus 2.019 GPa
292.8 ksi
23°C, 50% RH; ASTM D790
Izod Impact, Notched 7.35 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
13.8 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C

@Temperature -30.0 - 60.0 °C
50.0 µin/in-°F

@Temperature -22.0 - 140 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Equivalant
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Equivalant
Processing Properties Metric English Comments
Processing Temperature 260 - 280 °C
500 - 536 °F
Resin Temperature
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Drying Temperature 100 - 110 °C
212 - 230 °F
Pre-drying Temperature
Dry Time 3 - 4 hour
3 - 4 hour