Asahi Kasei Thermylene® P6-30FG-0632 30% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P6-30FG-0632 30% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 93.8 MPa | 13600 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 127 MPa | 18400 psi | ASTM D790 |
| Flexural Modulus | 5.10 GPa | 740 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.94 J/cm | 13.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0591 in thickness |
| Flame Spread | 30 mm/min | 1.2 in/min | Horizontal Burn Rate; FMVSS302 |