- Asahi Kasei Thermofil P-20TC-5100R 20% Talc Filled, Heat Stabilized
Asahi Kasei Thermofil P-20TC-5100R 20% Talc Filled, Heat Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermofil |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermofil P-20TC-5100R 20% Talc Filled, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 92 | 92 | ASTM D785 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Yield | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 49.6 MPa | 7200 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm | 0.500 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.74 J/cm | 7.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 59.4 µm/m-°C @Temperature 20.0 °C |
33.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 610 BT N 32 B PA610
- Old Hickory M&M Clays, Inc. Wilco-SLU Kaolin Clay
- Huntsman AVALON® 95 AHT DP Thermoplastic Polyurethane
- Lehmann & Voss LUVOCOM® 80-8222 Polyacetal-copolymer, with mineral filler, lubricant modified
- LG Chemical SSBR 2550H High Acrylonitrile Polymer
- Gromax BFG30-FH00B2 Nylon 6 30% Glass Filled (Conditioned)
- SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66
- Sylvin Technologies 6034-85 UV PVC Wire/Cable Compound
- Teknor Apex Telcar® TL-83-F912-E-UV Thermoplastic Elastomer
- 3M 4412N Extreme Sealing Tape
Copyright © lookpolymers.com All Rights Reserved