Asahi Kasei Tenac® GA510 Homopolymer Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Glass Fiber Reinforced |
| Manufacturer | Asahi Kasei |
| Trade Name | Tenac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac® GA510 Homopolymer Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber filled grade with high stiffness and superior dimensional stability.Information provided by Asahi Kasei Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in | Asahi Kasei Method |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in | Asahi Kasei Method |
| Melt Flow | 17 g/10 min | 17 g/10 min | ISO 1133 D |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 - 1 & - 2 |
| Elongation at Break | 20 % | 20 % | ISO 527 - 1 & - 2 |
| Tensile Modulus | 3.90 GPa | 566 ksi | ISO 527 - 1 & - 2 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 / 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 -1 & -2 flat |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75 -1 & -2 flat |
| Flammability, UL94 | HB | HB |