Asahi Kasei Tenac®-C 3510 Copolymer Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Impact Modified |
| Manufacturer | Asahi Kasei |
| Trade Name | Tenac®-C |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac®-C 3510 Copolymer Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-impact, high elongation grade, with increased molecular weightInformation provided by Asahi Kasei Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | Asahi Kasei Method |
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ISO 1133 D |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 63.0 MPa | 9140 psi | ISO 527 - 1 & - 2 |
| Elongation at Break | 60 % | 60 % | ISO 527 - 1 & - 2 |
| Tensile Modulus | 2.65 GPa | 384 ksi | ISO 527 - 1 & - 2 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 / 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 156 °C | 313 °F | ISO 75 -1 & -2 flat |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 -1 & -2 flat |
| Flammability, UL94 | HB | HB |