- Asahi Glass Fluon® P-810UP PFA Perfluoropolymer
Asahi Glass Fluon® P-810UP PFA Perfluoropolymer
| Category | Polymer , Thermoplastic , Fluoropolymer , PFA , Polyperfluoroalkoxyethylene, Molded/Extruded |
| Manufacturer | Asahi Glass Company |
| Trade Name | Fluon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Glass Fluon® P-810UP PFA Perfluoropolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent characteristics and similar properties of PTFE but can be processed using conventional thermoplastic techniques, such as extrusion molding, injection molding, blow molding, or electrostatic powder coating. And Fluon® PFA can be used in a wide range of temperatures from extremely low to high temperatures (260°C at the maximum) without losing its superior properties. Information provided by Asahi Glass Company, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.10 - 2.12 g/cc | 2.10 - 2.12 g/cc | ASTM D792 |
| Water Absorption | <= 0.030 % | <= 0.030 % | ASTM D570 |
| Melt Flow | 7.0 - 18 g/10 min | 7.0 - 18 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D1706 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Tensile Strength, Ultimate | 8.00 MPa @Temperature 250 °C |
1160 psi @Temperature 482 °F |
ASTM D638 |
| Elongation at Break | 410 % | 410 % | ASTM D638 |
| 600 % @Temperature 250 °C |
600 % @Temperature 482 °F |
ASTM D638 | |
| Flexural Modulus | 0.630 GPa | 91.4 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256A |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 130 µm/m-°C @Temperature 20.0 °C |
72.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Specific Heat Capacity | 1.046 J/g-°C | 0.2500 BTU/lb-°F | |
| Thermal Conductivity | 0.251 W/m-K | 1.74 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 305 - 315 °C | 581 - 599 °F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | >= 95 % | >= 95 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | ASTM D257 |
| Dielectric Constant | <= 2.1 @Frequency 60 Hz |
<= 2.1 @Frequency 60 Hz |
ASTM D150 |
| <= 2.1 @Frequency 1000 Hz |
<= 2.1 @Frequency 1000 Hz |
ASTM D150 | |
| <= 2.1 @Frequency 1e+6 Hz |
<= 2.1 @Frequency 1e+6 Hz |
ASTM D150 | |
| Dissipation Factor | <= 0.00020 @Frequency 60 Hz |
<= 0.00020 @Frequency 60 Hz |
ASTM D150 |
| <= 0.00020 @Frequency 1000 Hz |
<= 0.00020 @Frequency 1000 Hz |
ASTM D150 | |
| <= 0.00020 @Frequency 1e+6 Hz |
<= 0.00020 @Frequency 1e+6 Hz |
ASTM D150 | |
| Arc Resistance | >= 300 sec | >= 300 sec | ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Temperature, °C | 230 | |
| Flex Life, Cycles | 25000 |