Armstrong A-1/A Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Armstrong Epoxy Adhesives; Resin Technology Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Armstrong A-1/A Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A brown epoxy paste formulated with enhanced wetting capabilities to hard rubbers and rigid thermoplastics. Has low outgassing characteristics at temperatures below 250°FInformation provided by Ellsworth Adhesives.
Physical Properties Metric English Comments
Viscosity 430000 cP
430000 cP
Mixed
Mechanical Properties Metric English Comments
Hardness, Shore D 86
86
Tensile Strength, Ultimate 36.5 MPa
5300 psi
after optimum cure
Elongation at Break 1.3 %
1.3 %
Adhesive Bond Strength 32.4 MPa
4700 psi
Steel-Steel; after optimum cure
16.5 MPa

@Temperature -54.4 °C
2400 psi

@Temperature -66.0 °F
Aluminum-Aluminum tensile shear
16.5 MPa

@Temperature 25.0 °C
2400 psi

@Temperature 77.0 °F
Aluminum-Aluminum tensile shear
19.0 MPa

@Temperature 82.2 °C
2750 psi

@Temperature 180 °F
Aluminum-Aluminum tensile shear
Thermal Properties Metric English Comments
CTE, linear 34.0 µm/m-°C

@Temperature 20.0 °C
18.9 µin/in-°F

@Temperature 68.0 °F
Maximum Service Temperature, Air 121 °C
250 °F
Glass Transition Temp, Tg 103 °C
217 °F
Processing Properties Metric English Comments
Processing Temperature 22.2 °C
72.0 °F
73.9 °C
165 °F
Optimum cure is 2 hr. @ 165°F
Pot Life <= 30.0 min

@Temperature 25.0 °C
<= 30.0 min

@Temperature 77.0 °F
100 g
Descriptive Properties Value Comments
Color Brown
Mix Ratio 100/4
By Weight