- Arlon Thermabond® R36211A008 0.008" (0.203 mm) Uncured Silicone Rubber with Fiberglass Substrate
Arlon Thermabond® R36211A008 0.008" (0.203 mm) Uncured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | Thermabond® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon Thermabond® R36211A008 0.008" (0.203 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Generation II Thermabond® NP electrically insulating electronic adhesive. Bonds without primerDesign/Construction: Liner 1: Polyethylene Side 1: Uncured Silicone Rubber Substrate: Style 1080 Fiberglass Side 2: Uncured Silicone Rubber Liner 2: Polyethylene Appearance: Fiberglass fabric with blue silicone gum on both sidesThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 38.1 microns | 1.50 mil | Liner 1 |
| 38.1 microns | 1.50 mil | Liner 2 | |
| 63.5 microns | 2.50 mil | Side 1; Arlon SQA-TMS-003 | |
| 63.5 microns | 2.50 mil | Side 2; Arlon SQA-TMS-003 | |
| 76.2 microns | 3.00 mil | Substrate; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | Overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 55 | 55 | Silicone Property; ASTM D2240 |
| Tensile Strength | 5.17 MPa | 750 psi | Silicone Property; ASTM D412 |
| Elongation at Break | 400 % | 400 % | Silicone Property; ASTM D412 |
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property |
| Shear Strength | 2.76 MPa | 400 psi | Lap Shear Strength; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM E 831 |
| Specific Heat Capacity | 0.980 J/g-°C | 0.234 BTU/lb-°F | E 1461-01 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | Product Property; ASTM E 1530 |
| 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | Silicone Property; ASTM E 1530 | |
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -73.3 °C | -100 °F | |
| Glass Transition Temp, Tg | <= -100 °C | <= -148 °F | Silicone Property; ASTM D3418 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
D<sub>k</sub>, Silicone Property; IPC TM 650-2.5.5.3 |
| 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
D<sub>k</sub>, Product Property; IPC TM 650-2.5.5.3 | |
| Dielectric Strength | 39.0 kV/mm | 990 kV/in | ASTM D149 |
| Dissipation Factor | 0.0045 @Frequency 1.00e+6 Hz |
0.0045 @Frequency 1.00e+6 Hz |
D<sub>f</sub>, Silicone Property; IPC TM 650-2.5.5.3 |
| 0.0049 @Frequency 1.00e+6 Hz |
0.0049 @Frequency 1.00e+6 Hz |
D<sub>f</sub>, Product Property; IPC TM 650-2.5.5.3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Pressure 0.0689 - 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 10.0 - 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
| Shelf Life | 6.00 Month @Temperature 4.44 - 10.0 °C |
6.00 Month @Temperature 40.0 - 50.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Blue | |
| Total Product Weight (g/m2) | 240 | Arlon SQA-TMS-025 |