Arlon R38026B017 0.017" (0.432 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R38026B017 0.017" (0.432 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 1165 FiberglassSide 2: Uncured Silicone Rubber Interleave: LDPEThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	63.5 microns	2.50 mil	Side 1; Arlon SQA-TMS-003
	76.2 microns	3.00 mil	Interleave
	140 microns	5.50 mil	Substrate; Arlon SQA-TMS-003
	229 microns	9.00 mil	Side 2; Arlon SQA-TMS-003
	432 microns	17.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	73	73	Silicone Property; ASTM D2240
Tensile Strength	5.17 MPa	750 psi	Silicone Property; ASTM D412
Elongation at Break	252 %	252 %	Silicone Property; ASTM D412
Tear Strength	12.8 kN/m	73.0 pli	Die B, Silicone Property; ASTM D624
Peel Strength	0.263 kN/m	1.50 pli	Bond Strength (S2 to S2); Arlon SQA-TMS-011

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	3.00 Month @Temperature 7.22 °C	3.00 Month @Temperature 45.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Black
	Black	Substrate
	Gray	Substrate
Total Product Weight (oz/yd2)	18.3	Arlon SQA-TMS-025